Beep 6211 two part epoxy structural adhesive
- Resistance of moisture, pollution and other atmospheric constituent
- High tensile, excellent adhesive property
- Excellent pollution resistance, low demand of surface pretreatment
- No solvent, no curing by-products
- Excellent high and low temperature resistance (-50~150°C)
- Medium viscosity, good operational process
- Good adhesion to fiberglass cloth, steel plate etc
FEATURES
Beep 6211 is a room temperature curing or heat curing epoxy structural adhesive. It has following properties after cured with mixture ratio 1:1 of weight
| PROPERTY | STANDARD/UNITS | VALUE of Beep 6211 | |
| —- | —- | PART A | PART B |
| Appearance | Visual inspection | Black viscous paste | Beige viscous paste |
| Viscosity | 25°C, cps | 80,000 | 55,000 |
| Density | 25°C, g/cm3 | 1.35 | 1.35 |
| Mixture ratio | Mass ratio | A:B=1:1 | |
| Viscosity of mixture | 25°C, cps | Thixotropic paste | |
| Mixture density | 25°C, g/cm3 | 1.35 | |
| Operation time | 25°C, min | 10 (tested based on 100g mixture) | |
| Cure condition | RTV/HEAT | 25°C/ 70 min; 60°C/ 20 min | |
| Hardness | Shore D | 90 | |
| Shear strength | Al/Al, MPa | 17 | |
| Thermal conductivity | W/mK | 0.4 | |
For bonding of Metal, SMC glass fiber reinforced plastic parts, Aluminum honeycomb panel, Motor iron core, Nomex paper bonding, high-speed rail track repairing, metal and plastic of rail transportation, metal and composite material bonding etc.
USE
-
- Stir part A and part B separately in the origin container before taking to mix, keep sealed after taking.
- Mixing and stirring the mixture at same direction, or there will be too many air inside the adhesive;The adhesive at the frame and bottom of container should be stirred well, or there will lead to somewhere uncured.
- The temperature is too low will lead to low curing speed, heat cure is recommended. When unable to achieve an initial strength, constant temperature control is required on site.
- The curing process is an exothermic reaction; the amount of adhesive impact the operation time. Above operation time of 100g is just for reference.